Tactus velamentum operimentum vitri, tange tabula vitri, Lens operculum
Technical data
vitrum aluminosilicatum | Nitri vitreum calcis | |||||
Type | corning muta vitrum | dragontrail vitrum | Schott Xensat | panda vitrum | NEG T2X-1 glass | supernatet vitrum |
Crassitudo | 0.4mm,0.5mm,0.55mm,0.7mm 1mm,1.1mm,1.5mm,2mm | 0.55mm,0.7mm,0.8mm 1.0mm,1.1mm,2.0mm | 0.55mm,0.7mm 1.1mm | 0.7mm,1.1mm | 0.55mm,0.7mm 1.1mm | 0.55mm,0.7mm,1.1mm,2mm 3mm,4mm,5mm,6mm |
Confortatus eget | DOL≥ 40um CS≥700Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 32um CS≥600Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 8um CS≥450Mpa |
duritia | ≥9H | ≥9H | ≥7H | ≥7H | ≥7H | ≥7H |
Transmittance | >92% | >90% | >90% | >90% | >90% | >89% |
Superficies curatio: Anti fulgor vestitur, anti vestis reflexiva, anti fingerprints, ito tunica promptiva prompta.
Optio temperata: Thermaliter temperatur, calor confortatur, chemica roboratur (chemice temperatur).
Processing
Type operculum Vitri
1. Aluminosilica vitrum refert ad vitrum cum silica et alumina tanquam principales partes, in quibus alumina contenta plus quam 20% attingere potest.Coordinatio numerus aluminii ion dependet ab R2O (oxide metallico alcali) contento.
Felis Vitrum a corninge unum vitreum aluminosilicate kinf est. ob hanc in superiori observantia.
Superior nodus resistens boni chemicae stabilitatis;
electrica velit
mechanica vires
humilis scelerisque expansionem coefficiens
caliditas viscositas.
Magno pretio
Late in genere tactus velorum et telephonicorum, vel in aliis machinis portatilis, late adhibetur.
Vitreum calcis nitri, forma vitrei usitatissima producta, vilis est, chemica stabilis, rationabiliter dura, et vitrum perquam operabile, satis est ad postulationem fundamentalem, quae maxime populare et late in variis applicationis tactus usum faciunt.
STEPHANT VITREI VS, AESTUM VITREA CONTINET VITREA CONTINENTUR.
Quae differentia est inter scelerisquely temperatam et chymicam vitream roboratam.