1.ultra vitrum purum habet multum inferiorem vitri sui explosionis ratio
Definition of auto-explosionis: Vitri temperati sui explosio est phaenomenon comminutio quae sine vi externa fit.
Principium explosionis centrum est et radiatim in circumfusum diffunditur.In exordio sui explosionis duo fragmenta relative magna erunt cum proprietatibus "papilii macularum".
Causae explosionis sui: Explicatio vitri temperati sui saepe causatur ex existentia nonnullorum lapidum minutorum in scheda vitri temperati originali.Temperatus cristallinus status calidissimus (a-NiS) est "gelidus" in productione vitrea et in temperatura ambiente custoditur.In vitro temperato, cum hic status crystallinus summus temperatus non stabilis sit in cella temperie, paulatim in statum normalem crystallinum (B-NiS) transfigurabit cum tempore, et quodam dilatationis volumine comitatus erit (2~. 4% dilatatio) in transmutatione.;Si lapis sita est in area distrahentes in vitro temperato, haec crystalli phase transmutatio saepe efficit ut vitrum temperatum subito frangatur, quod est quod plerumque vitri temperati explosionem sui ipsius appellare consuevimus.
Auto- explosio rate of ultra vitrum temperatum perspicuum: Quia ultra vitreum vitreum altum puritate materiae rudis utitur, immunditia compositio ad minimum reducitur, et compositio niS correspondens multo humilior est quam vitrei ordinarii innatantia, ita sui ipsius. -explosio rate attingere potest intra 2/, circa 15 tempora inferiora cum 3‰ auto-explosione rate ordinaria vitro perspicuo.
2. Color constantia
Cum ferrum in materia rudis contentum tantum 1/10 vel etiam minus quam vitri ordinarii, ultra-lucidum vitreum minus viridis necem in luce visibili quam vitreo ordinario haurit, constantiam vitrei coloris procurans.
3. Ultra vitrum perspicuum habet maiorem transmissionem et coefficientem solarem.
| ultra patet vitrum parametri | |||||||||||||
| Crassitudo | transmissio | Reflexio | solaris radiatio | colorum coefficiens | Ug | soundproofing | UV transmissio | ||||||
| recta penatrating | reputans | effusio | total | shortwave | longwave | total | (W/M2k) | Rm (dB* | Rw（dB) | ||||
| 2mm | 91.50% | 8% | 91% | 8% | 1% | 91% | 1.08 | 0.01 | 1.05 | 6 | 25 | 29 | 79% |
| 3mm | 91.50% | 8% | 90% | 8% | 1% | 91% | 1.05 | 0.01 | 1.05 | 6 | 26 | 30 | 76% |
| 3.2mm | 91.40% | 8% | 90% | 8% | 2% | 91% | 1.03 | 0.01 | 1.05 | 6 | 26 | 30 | 75% |
| 4mm | 91.38% | 8% | 90% | 8% | 2% | 91% | 1.03 | 0.01 | 1.05 | 6 | 27 | 30 | 73% |
| 5mm | 91.30% | 8% | 90% | 8% | 2% | 90% | 1.03 | 0.01 | 1.03 | 6 | 29 | 32 | 71% |
| 6mm | 91.08% | 8% | 89% | 8% | 3% | 90% | 1.02 | 0.01 | 1.03 | 6 | 29 | 32 | 70% |
| 8mm | 90.89% | 8% | 88% | 8% | 4% | 89% | 1.01 | 0.01 | 1.02 | 6 | 31 | 34 | 68% |
| 10mm | 90.62% | 8% | 88% | 8% | 4% | 89% | 1.01 | 0.02 | 1.02 | 6 | 33 | 36 | 66% |
| 12mm | 90.44% | 8% | 87% | 8% | 5% | 88% | 1.00 | 0.02 | 1.01 | 6 | 34 | 37 | 64% |
| 15mm | 90.09% | 8% | 86% | 8% | 6% | 87% | 0.99 | 0.02 | 1.00 | 6 | 35 | 38 | 61% |
| 19mm | 89.73% | 8% | 84% | 8% | 7% | 86% | 0.97 | 0.02 | 0.99 | 6 | 37 | 40 | 59% |
4. ultra vitrum perspicuum habet transmissionem UV inferiorem
| patet vitrum parametri | |||
| Crassitudo | transmissio | Reflexio | UV transmissio |
| 2mm | 90.80% | 10% | 86% |
| 3mm | 90.50% | 10% | 84% |
| 3.2mm | 89.50% | 10% | 84% |
| 4mm | 89.20% | 10% | 82% |
| 5mm | 89.00% | 10% | 80% |
| 6mm | 88.60% | 10% | 78% |
| 8mm | 88.20% | 10% | 75% |
| 10mm | 87.60% | 10% | 72% |
| 12mm | 87.20% | 10% | 70% |
| 15mm | 86.50% | 10% | 68% |
| 19mm | 85.00% | 10% | 66% |
5. ultra vitrum limpidum difficultatem productionis altioris habet, sic sumptus vitrei claris altior est
Ultra vitrum vitrum clarum excelsum qualitatem habet ad vicus arenae ingredientes, etiam alta requisita pro ferro contento, chalcitis harenae naturalis ultra-alba vicus vix est relative, et ultra vitrum clarum relative altum technologicum habet, productionem moderandi difficultatem facit. est circa 2 tempora altior quam vitro puro.